ZINEP® 80

Description

Recommended use

Anticorrosive protection of steel structures operating under atmospheric conditions of all macroclimatic regions, atmosphere types and location categories as per GOST 15150. The coating is resistant to sea and fresh water, aqueous solutions of salts, to oil and oil products.

Recommended for use:

• with ISOLEP-mio, POLYTON-UR (UV), POLYTON-UR, ALUMOTAN, as well as with other epoxy, polyurethane, vinyl chloride and copolymer-vinyl chloride coatings;

• in complex fire-proof systems with the of the PLAMCOR^® series

Certificates, approvals

Certificate of state registration No. RU.66.01.40.015.Е.000120.10.19 dated 04.10.2019.

Lacquer Coating Research Institute, Khotkovo town.

Surface preparation

• to degrease metal surface to 1 grade according to GOST 9.402;

• perform abrasive blasting cleaning of scale, rust and traces of old paint to not less than 2 grade according to GOST 9.402 or Sa 2 ¹/₂ ISO 8501-1 with a roughening of 30-50 μm (between segments 1 and 2. but lower of G comparator ISO 8503-2). Application on a smooth surface is not allowed;   

• to remove dust.

The primer should be applied no later than 6 hours after abrasive blasting.
In case of storing the primer at a lower temperature, it is necessary to hold the material for 24 hours at temperature from plus 15 to plus 25 °C.
Before the application of subsequent layers, the coated surface must be clean from dirt, degreased, dust-free and dry.

Application

• mix the primer base to a homogeneous condition before application;
• add hardener to the primer base with constant stirring, mix thoroughly during 2-3 minutes to a homogeneous condition. The proportion of base and hardener: by mass 100:5.5, by volume 6:1;
• hold for at least 30 minutes before application and mix again to a homogeneous condition;
• dilute to working viscosity, if necessary, immediately before application.

It is recommended to apply the ZINEP 80 at temperature from 0 to plus 40 °C (allowed at temperature from minus 5 °C) and relative humidity of not more than 85 %. The temperature of the surface to be painted must be above the dew point by at least 3 °C, but not above plus 40 °C. When painting, the temperature of the material should not be below plus 15 °C.

The drying time "to turning over, handling", "to stackable" depends also on the design features of the metal structures (the number of support points, sling arrangements, metal structures fasteners for further transportation) and may differ from those indicated. It should be determined by test coloring for specific conditions.

The maximum holding time before coating application is not more than 1 year. The holding time of the coating at a temperature of 20 °C before the operation in severe environments is not less than 7 days.

Storage and handling

ZINEP 80 is supplied as the Base in 10 and 1 litre metal containers and the curing agent in 3 and 0.25 litre metal containers.

Storage conditions – according to GOST 9980.5 (at air temperature from minus 40 to plus 40 °C). The material components shall be stored away from heat sources, the container shall be protected from direct sunlight (short-term impact, not more than 3 hours, is acceptable) and atmospheric condensation.

The shelf life of the components is 18 months starting with the date of manufacture.

Precautions

When working with the enamel-primer one shall observe the existing sectoral standard norms and requirements and safety measures as specified on the package label.

One shall use personal protective equipment (goggles, face masks and respirators) and avoid inhalation of solvents and contact of the composition substances with skin, eye mucosa, respiratory channels; use inside the premises is allowed only in case sufficient ventilation is provided.

It is classified as fire-hazardous material.