REPRESENTATIVE OFFICE
IN YOUR REGION
VMP Holding CISC
Ekaterinburg,
25 Tkachey str.,

tel.: +7 343 357-30-97,
+7 343 357-30-79
e-mail: office@fmp.ru



VMP in social networks:

QUICK-DRYING
MATERIAL
ATMOSPHERE-RESISTANT
MATERIAL
HEAT-RESISTANT
MATERIAL
THICK-LAYERED
MATERIAL
FOR APPLICATION AT
NEGATIVE
TEMPERATURE
SINGLE-PACKED
MATERIAL
ST 2, ST 3 SURFACE
PREPARATION DEGREE
FOR USE AT
SEA AND FRESH
WATER
FOR USE WHEN
EXPOSED TO OIL
AND OIL PRODUCTS
ZINC-FILLED
MATERIAL
MATERIAL WITH
ANTICORROSIVE
PIGMENTS
MATERIAL WITH
CORROSION INHIBITOR
MATERIAL WITH
ANTISTATIC PROPERTIES

ISOLEP®-oil Composition

ISOLEP-oil
TU 20.30.12-081-12288779-2017
Composition
Two-packed
Colour: gray

Description

Two-packed epoxy composition, consisting of a base and a hardener. The base is a suspension of pigments, extender and functional additives in a solution of a modified epoxy resin in a mixture of organic thinners. Hardener – aliphatic polyamine resin.

Recommended use

It is used as an independent coating for anticorrosive protection of the internal surface of steel tanks, reservoirs, tank cisterns, industrial pipelines that come into contact with crude oil and commercial oil, fuel oil; bottom, sea and fresh water; chemical solutions with weak acid medium (pH 5-7) and weakly alkaline (pH 8-11) media, washing fluids.
It is characterized by a high content of non-volatile matters, makes it possible to obtain a highbuild abrasion-resistant coating with high protective properties. The recommended operating temperature is up to plus 60 °С (for a short time it is allowed up to plus 75 °С, it can stand steaming operation).
The light color of the coating (gray) simplifies the process of inspecting and accepting the coating on the inner surface of tanks and reservoirs.

Certificates, Approvals

Certificate of state registration No. RU.66.01.40.015.Е.000124.07.18 dated 05.07.2018.
The Register of core products of PJSC "Transneft".
Decision of All-union Pipeline Construction Scientific and Research Institute for heavier-duty coating with a projected working life of 20 years.

Surface preparation

  • to degrease metal surface to 1 grade according to GOST 9.402;
  • to do abrasive blast cleaning of scale and corrosion to grade not less than 2 according to GOST 9.402 (Sa 2½ according to ISO 8501-1). Surface profile is sharp, angular with a roughness of 85-115 µm (segment 3G according to ISO 8503-2);
  • to remove dust.
Reducing the surface preparation grade and application on a smooth surface without a roughening is not allowed. The allowed interval between preparation of the surface and application of the first coating layer should not exceed 6 hours in the absence of sweating on the surface and exclusion of any variety of contamination.

Application

  • mix the base to a homogeneous condition before application;
  • add a hardener to the base (mixing ratio of base and hardener: 3.6:1 by volume);
  • mix thoroughly with an electric mixing machine.
The pot life of the material (after mixing the components) at ambient temperature (20±2) °C is not less than 1 hour (for the organization of painting, the decrease of the pot life with increasing temperature should be taken into account). 
The material may be applied at an ambient temperature of plus 5 to plus 40 °C (recommended from plus 5 to plus 30 °C) and relative humidity not more than 80 %. The temperature of the surface to be painted must be above the dew point by at least 3 °C, but not above plus 40 °C.
When painting, the temperature of the material must be not less than plus 15 °C.
Application by airless spray is recommended in 1 layer, brush or roller – 2-3 layers allowed. Drying  of the coating is natural. As the temperature increases, the drying time shortens. Drying time "to tack free", as well as the time for complete hardening (drying for service) are given in the table (for a dry film thickness of 300 μm).

Storage and handling

The composition is delivered in packages: base and hardener packed in metal buckets.
Storage and transportation conditions – in accordance with GOST 9980.5 at air temperature from minus 40 to plus 40 °C. When storing the container should not be exposed to atmospheric precipitation and direct sunlight, short-term storage of the container under direct sunlight is allowed, but not more than 3 hours.
Shelf life in hermetically enclosed containers while meeting the requirements: the composition base (24 months) and hardener (12 months) starting with the manufacture date.

Precautions

When working with the composition, the existing sectoral standard norms and requirements and safety measures as specified on the package label shall be observed.
Personal protective equipment (goggles, face masks and respirators) should be used, and inhalation of thinners and contact of the composition with skin, ocular mucosa, respiratory channels shall be avoided; use inside the premises is allowed only in case sufficient ventilation is provided.
The composition and its components (base and hardener) are fire-hazardous!
The hardened coating is not harmful to human health.

The information is of general character, without consideration to the object specific nature. Use of materials for other purposes not specified here or in case other influencing factors are present shall be approved by the  VMP Holding CJSC  in writing. In case of absence of such approval the manufacturer is not held liable for the improper use of the material and the buyer falls from the right to present claims connected with the coating quality

.